Product Description
Good fluidity, easy to level, it can reproduce subtleties, and the reproduction effect is good;
Easy to operate, it can be operated by hand or machine;
Good tensile force, strong tear resistance, and high elongation;
Shrinkage rate is less than 0.3%, it is acid and alkali resistance and aging resistance;
It has many times of mold turning, long service life, and the liquid silicone molds made are not deformed;
Color, hardness, viscosity, and operating time, can be adjusted as needed.
Usage
Jelly candle mould
Jelly candle molds
Festive candle molds
Birthday wedding candle molds
Christmas candle mould, DIY candle mould
Model | Viscosity(cps) | Hardness(Shore A) | Density (g/cm³) | Resilience (%) | Tensile strength (MPa) | Elogation at break (%) | Tear strength (KN/m) | Tensile set(%) | Line shrinkage (%) |
Test Standard | DIN53019 | GB/T531.1 | GB/T533-2008 | GB/T1681- 2009 | GB/T528 | GB/T528 | GB/T529 | GB/T528 | CGB-T14235.4 |
YR250-30MJ AB | 50 | 40 | 1.09 | 70 | 7 | 400 | 30 | 0.8 | 2.1 |
YR250-43MJ AB | 50 | 40 | 1.09 | 70 | 7 | 400 | 30 | 0.8 | 2.1 |
YR250-45MJ AB | 45 | 45 | 1.08 | 65 | 7 | 400 | 30 | 0.9 | 2.2 |
YR250-40MJ AB | 45 | 40 | 1.09 | 68 | 7 | 420 | 30 | 0.9 | 2.1 |
YR250-35MJ AB | 35 | 35 | 1.07 | 65 | 7 | 380 | 30 | 0.8 | 2.0 |
YR250-40MJ AB | 40 | 40 | 1.08 | 60 | 6.85 | 400 | 30 | 0.9 | 2.1 |
Remark | Vulcanization conditions: A/B is evenly mixed, Mold:140mm×120mm×2mm,175℃×5min compression molding. Assistance with specifications is available by contacting our engineers. |
Related certificate
FDA,MSDS,RoHS, REACH, etc.
Colors
Translucent, Milk white, Clear, and so on.
Can be customized color.
External packing
25KG,20KG,200KG/ pail or Customized.
Store and Caution
In order to prevent the physical properties of silicone rubber from changing, We recommend customers not add silicone oil;
After the liquid silicone mold is made, it is recommended to store it 24 hours before putting it into production. So it can achieve the best use effect;