High Temperature Liquid Silicone Rubber for Carbon Fiber Molding
High Temperature Liquid Silicone Rubber for Carbon Fiber Molding High Temperature Liquid Silicone Rubber for Carbon Fiber Molding
High Temperature Liquid Silicone Rubber for Carbon Fiber Molding High Temperature Liquid Silicone Rubber for Carbon Fiber Molding

loading

High Temperature Liquid Silicone Rubber for Carbon Fiber Molding

Carbon fiber composite molded liquid silicone is a high-temperature mold silicone with low cost, simple operation, high temperature resistance and shrinkage resistance. This kind of liquid silicon rubber is generally used with a hardness above Shore 30A and has excellent tear resistance.

Model Number:                    YR250-45MJ AB
Viscosity(cps):                 50
Hardness(Shore A):           45
Mix ratio(A/B):               50:1
MOQ(KG):                            200 Kilograms
Storage life:                         12 Months
Application:                          Carbon Fiber Molded Silicone
Apprearance:                       Two part liquid
Certificate:                         FDA,MSDS,RoHS, REACH and so on.
Lead Time:                           7-10 days
Payments:                            L/C, T/T
Supply Ability:                      100 Tons/day
Package:                              20KG/25KG/200KG drum+Pallet
Transport :                           Sea shipment, Air shipment
SKU:
Availability:
Quantity:

Product Description

Features

It can withstand temperatures of 300-400 degrees in an instant.

Low shrinkage rate and no low molecules being released during the cross-linking process, so the volume remains unchanged, and the shrinkage rate is less than 0.1%.

Good fluidity, easy to pour; It can be cured at room temperature or heated, and it is easy to operate.

High tear strength, no deformation, and aging.


Application

Carbon Fiber Molded Silicone, wind turbine blade complex mold, ship complex mold, aerospace, sanitary ware, epoxy resin, unsaturated resin, PU, ABS, cement gypsum, and other product fields.


Product Parameter


Model

Viscosity(cps)Hardness(Shore A)

Density

(g/cm³)

Resilience

(%)

Tensile strength

(MPa)

Elogation 

at break

(%)

Tear strength

(KN/m)

Tensile set(%)

  Line 

shrinkage

(%)

   Test Standard

DIN53019

GB/T531.1GB/T533-2008GB/T1681- 2009GB/T528GB/T528GB/T529GB/T528  CGB-T14235.4
YR250-30MJ AB50
401.09707400300.82.1
YR250-43MJ AB50
401.09707400300.82.1
YR250-45MJ AB45451.08657400300.92.2
YR250-50MJ AB45451.09656.5400300.92.1
RemarkVulcanization conditions:A/B is evenly mixed,Mold:140mm×120mm×2mm,175℃×5min compression molding.Assistance with specifications are available by contacting our engineers.


Certificate

FDA,MSDS,RoHS, REACH, and so on.


Color

Clear and milk white(standard colors)

Other wide variety of colors (customized)


Spec

25KG,200KG/ pails or Customized.


How to use

Silicone molding method: perfusion mold, brush mold (sheet mold).

The curing ratio is: 50:1( A is silicone rubber, and B is a curing agent). After vacuum defoaming, the mold can be brushed or filled.

Addition type liquid silicone can be used for high-precision products, and the curing ratio is 1:1, which can be cured at room temperature or quickly cured by heating.


Shelf-life

It can be stored unopened for 12 months at a room temperature of 25°C. 

It should be stored in a dry bath at room temperature and in an airtight container and do not contact with water to prevent deterioration.