Product Description
Features:
Tear strength
Fast vulcanization
Good soft hand feeling
High and low-temperature resistance
Prodcut Application
Silicone pacifiers Teether
baby bottles
baby tableware
Breast pump
Baby finger toothbrush
Product Parameter
Model | Viscosity（cps） | Hardness（Shore A） | Density (g/cm³) | Resilience (%) | Tensile strength (MPa) | Elogation at break (%) | Tear strength (KN/m) | Tensile set(%） | Line shrinkage (%) |
| Test Standard | DIN53019 | GB/T531.1 | GB/T533-2008 | GB/T1681- 2009 | GB/T528 | GB/T528 | GB/T529 | GB/T528 | CGB-T14235.4 |
| YR250-10 AB | 500 | 10 | 1.07 | 20 | 1.5 | 750 | 5 | 4.3 | 2.5 |
| YR250-10 AB | 600 | 15 | 1.08 | 45 | 3.5 | 850 | 9.0 | 3.4 | 2.7 |
| YR250-10 AB | 600 | 18 | 1.08 | 50 | 5 | 800 | 12 | 3.4 | 2.5 |
| YR250-10 AB | 800 | 21 | 1.09 | 50 | 6.5 | 800 | 15 | 2.6 | 2.4 |
| YR250-10 AB | 1000 | 30 | 1.1 | 55 | 7 | 700 | 15 | 2.6 | 2.4 |
| YR250-10 AB | 1200 | 40 | 1.11 | 55 | 7.5 | 550 | 25 | 2.6 | 2.5 |
| YR250-10 AB | 1200 | 50 | 1.12 | 65 | 9 | 550 | 30 | 1.7 | 2.6 |
| YR250-10 AB | 1500 | 60 | 1.12 | 60 | 9.5 | 500 | 35 | 1.7 | 2.6 |
| YR250-10 AB | 2000 | 65 | 1.13 | 55 | 9.5 | 400 | 30 | 0.8 | 2.5 |
| YR250-10 AB | 2500 | 70 | 1.13 | 55 | 9 | 350 | 25 | 0.8 | 2.5 |
| Remark | Vulcanization conditions：A/B is evenly mixed，Mold:140mm×120mm×2mm,175℃×5min compression molding.Assistance with specifications are available by contacting our engineers. | ||||||||
Certification
REACH,FDA,RoHS MSDS, ISO9001:2015
Colors:
Standard colors:Clear
Can be customized
Package:
20KG/Pail
25KG/Pail
200KG/Pail
Storage and Cautions
Clear silicone liquid can be stored for 6 months at room temperature. In the process of use, it can not be mixed with water, impurities, condensed type silicone rubber organotin catalyst, acid, alkali and other organic compounds containing sulfur, phosphorus, nitrogen, otherwise affect the curing of the rubber.